6005 alloy is widely used for extrusion of general aluminum material. All extruded sections and pipes that require material strength more than 6063 alloy can be produced by this alloy. Like 6063 alloy, they are pure Al-Mg-Si alloy. Except Mg and Si, no alloying elements are contained, Mg2Si is the only strengthening phase, and all Mg and Si form Mg2Si. It has excellent extrusion performance and low quench sensitivity, and can be used for on-line quenching of the extruder. The material with wall thickness less than 3mm can be air-cooled quenching. Another prominent advantage of them is the smooth surface and easy anodizing and coloring. 6005 alloys are currently widely used for extruding sections and pipes of products such as ladders, wheelchairs, television antennas, and platform frames. However, it should be noted that 6005 alloys are not made to bear the impact load structure.





6005 aluminum tube pipe is widely used for extrusion of general aluminum material. All extruded sections and pipes that require material strength more than 6063 alloy can be produced by this alloy. Like 6063 alloy, they are pure Al-Mg-Si alloy. Except Mg and Si, no alloying elements are contained, Mg2Si is the only strengthening phase, and all Mg and Si form Mg2Si. It has excellent extrusion performance and low quench sensitivity, and can be used for on-line quenching of the extruder. The material with wall thickness less than 3mm can be air-cooled quenching. Another prominent advantage of them is the smooth surface and easy anodizing and coloring. 6005 aluminum tube pipe are currently widely used for extruding sections and pipes of products such as ladders, wheelchairs, television antennas, and platform frames. However, it should be noted that 6005 alloys are not made to bear the impact load structure.







Specification:
Alloy: 6005 6105 6041 6042
Temper: T1、T5、T6511
OD: 3--130mm
ID: 3--100mm
Length: 1000mm--6000mm

Chemical Composition
Alloy Si Fe Cu Mn Mg Cr Ni Zn Ga V Ti Other Min.Al
6005 0.6-0.9 0.35 0.10 0.10 0.40-0.60 0.10 - 0.10 - - 0.10 0.15 Remainder
6105 0.6-1.0 0.35 0.10 0.10 0.45-0.8 0.1 - 0.1 - - 0.1 0.15 Remainder
6041 0.5-0.9 0.15-0.70 0.15-0.60 0.05-0.20 0.8-1.2 0.05-0.15 - 0.25 - - 0.15 0.15 Remainder
6042 0.5-1.2 0.70 0.2-0.6 0.40 0.7-1.2 0.04-0.35 - 0.25 - - 0.15 0.15 Remainder

Physical Property
Alloy Temper Wall thickness
/mm
Room temperature Test Result
Tension Strength/MPa Yield Strength/MPa Elongation/%
A50mm A
Not less than
6005
 
T1 ≤12.50 170 105 16 14
T5 ≤3.20 260 240 8 -
3.20~25.00 260 240 10 9
6105 T1 ≤12.50 170 105 16 14
T5 ≤12.50 260 240 8 7
6041 T5、T6511 10.00~50.00 310 275 10 9
6042 T5、T6511 10.00~12.50 260 240 10 -
12.50~50.00 290 240 - 9