7075 T6 seamless aluminium aluminum alloy Pipe tube is a cold-treated forging alloy with high strength, far better than soft steel. 7075 is one of the most powerful commercial alloys. After heat treatment, very high strength characteristics can be achieved.
7075 T6 seamless aluminium aluminum Pipe tube are generally added with a small amount of copper, chromium and other alloys. Among them,
7075-T651 aluminum alloy is the most superior one. It is known as the best product of aluminum alloy, with high strength and far superior to any mild steel. The alloy has good mechanical properties and anodic reaction.
The specification of
7075 T6 seamless aluminium aluminum Pipe tube
Typical alloy: 7075 aluminium tube
Material status: O, T6, T651, T7451
Extrusion Pipe: External Diameter 20mm~300mm
Seamless Pipe: Outer Diameter 20mm~600mm
Large Caliber Aluminum Tube: Customized
Typical products: die processing, mechanical equipment, fixture, aerospace industry, blow moulding (bottle) mould, ultrasonic plastic welding mould, golf ball head, etc.
The strength of
7075 T6 seamless aluminium aluminum Pipe tube
Shear strength: alloy (bare) and clad aluminium alloy, O state: 152 MPa (22ksi); alloy (bare) T6, T7451 state: 331 MPa (48ksi); clad aluminium alloy T6, T7451 state: 317 MPa (46ksi)
Hardness: O shape: 60HB; T6, T651 state: 150HB;
The data were obtained from the test results of 10 mm diameter ball and 30 seconds under 500 kg load.
Poisson's ratio: 0.33.