The intorduce of
2014A T6511 aluminum tube pipe
2014A T6511 aluminum tube pipe with alloy elements of copper, molybdenum is called hard machining performance, high strength and good,
2014A T6511 aluminum tube pipe used in high strength and hardness (including high temperature) of the occasion, also known as the 2 Department of military application for aluminum, heavy forgings, plate and extrusion materials used in aircraft the structure, the first stage rocket fuel tank and multi spacecraft parts, wheels, truck frame and suspension parts.
The Chemical elements of
2014A T6511 aluminum tube pipe
Cu3.8-5.0,
Si0.5-0.90,
Fe0.5-,
Mn0.4-1.20,
Mg0 .2-0.8,
Zn0.25-,
Cr0.1-,
Ti0.15-
Al:Remainder
The Mechanical properties of
2014A T6511 aluminum tube pipe
Tensile strength：Min 460 Mpa
Proof Stress：Min415 Mpa
Hardness：140HB
Elongation：Min7%
The Generic Physical Properties of
2014A T6511 aluminum tube pipe
Density :2.82 g/cm3
Thermal Expansion :23 x 10 -6/K
Melting Point:535℃
Modulus of Elasticity:71 Gpa
Thermal Conductivity:138 W/m.K